STUDIO

Cigna Black Studio Plywood is a versatile building material with applications in many interior and exterior surfaces. It is one of the most durable materials available and it can provide an excellent foundation for your building. We have been providing the best quality Cigna Black Studio Plywood for over 55 years. All the timbers that we use are hand-picked from forests across the world. These timbers are seasoned and chemically treated to make our Cigna Black Studio Plywood durable, long lasting and resistant to termites and borers. These then undergo a unique THT treatment, a technique that ensures optimum treatment of moisture.

STUDIO

logo Cigna Black Plywood

Outfitted with a modern infrastructure, we are known as the most important manufacturer, wholesaler, distributor, retailer, and supplier of supreme quality Decorative Veneer Plywood. The presented Studio plywood is accessible in standard as well as modified option. These Studio plywood are processed from quality assured raw material and highly updated technology. We guarantee our customers that our offered veneer plywood is quality examined and are given in large quantities at economical rates.

We are the leading manufacturer, wholesaler and supplier of a quality-assured range of Commercial Studio Plywood. This Studio Plywood is manufactured by using the finest quality wood and other allied material and using the advanced technology in line with set industry standards. Apart from this, our offered veneer is largely used in furniture industry to provide different types of products. We offer this excellent quality veneer in different size and shape to fulfill the needs of our clients. These Studio Plywood are also tested on various quality parameters to assure its quality and reliability.

logo Cigna Black Plywood

 

 

S.No. Test I.S. : 303 Requirement Cigna Black Results
1 Moisture Content 5-15% 8-10%
2 Glue Adhesion Test Three test specimens of size 250mm x 100mm shall be prepared and submerged in water at 60 +/- 2 Centigrade for Three Hours and then Dryed for Eight Hours at a temperature of 65 +/- 2 Centigrade followed by Two more cycles and then tested as per IS:1734 (Part 5) 3 cycles carried out. No delamination observed. Excellent Bonding.
3 Modulus of Elasticity Across the Grains - Average 2000 N/mm2 2800 N/mm2
4 Moe Min. Pass standards Excellent